Abrasive Wear Resistance of the Iron- and WC-based Hardfaced Coatings Evaluated with Scratch Test Method
Journal Title: Tribology in Industry - Year 2013, Vol 35, Issue 2
Abstract
Abrasive wear is one of the most common types of wear, which makes abrasive wear resistance very important in many industries. The hardfacing is considered as useful and economical way to improve the performance of componentssubmitted to severe abrasive wear conditions, with wide range of applicable filler materials. The abrasive wear resistance of the three different hardfaced coatings (two iron‐based and one WC‐based), which were intended to be used for reparation of the impact plates of the ventilation mill, was investigated and compared. Abrasive wear tests were carried‐out by using the scratch tester under the dry conditions. Three normal loads of 10, 50 and 100 N and the constant sliding speed of 4 mm/s were used. Scratch test was chosen as a relatively easy and quick test method. Wear mechanism analysisshowed significant influence of the hardfaced coatingsstructure, which, along with hardness, has determined coatings abrasive wear resistance.
Authors and Affiliations
A. Vencl, B. Gligorijević, D. Džunić
Keywords
Related Articles
- EP ID EP156713
- DOI -
- Views 106
- Downloads 0
Fabrication of LM25/SiO2 Metal Matrix Composite and Optimization of Wear Process Parameters Using Design of Experiment
LM25 aluminium alloy reinforced with 15 wt% SiO2 metal matrix composite was fabricated by liquid metallurgy technique. Microstructure of the fabricated composite specimen was observed using inverted metallurgical microsc...
Investigation of Abrasive Wear Performances of Different Polyamides by Response Surface Methodology
This study presents the investigation of abrasive wear performances for polyamides using a Response Surface Methodology (RSM). Tests were carried out in a pin-on-disc using various conditions against SiC abrasive cloth....
Tribocorrosion Behavior of Niobium-Based Thin Films for Biomedical Applications
The current work presents a comparative study of niobium, niobium carbide, and niobium nitride coatings deposited on AISI 316LVM stainless steel. The investigation was based on the synergy between corrosion and wear; the...
Tribological Characterisation of PBT + Glass Bead Composites with the Help of Block-on-Ring Test
The materials involved in this research study were produced by die moulding in order to obtain bone samples type 1A (SR EN ISO 527‐ 2:2003). These composites have a matrix of polybutylene terephthalate (PBT) commercial g...
Steady State Thermo-Hydrodynamic Analysis of Two-Axial groove and Multilobe Hydrodynamic Bearings
Steady state thermo-hydrodynamic analysis of two axial groove and multi lobe oil journal bearings is performed in this paper. To study the steady state thermo-hydrodynamic characteristics Reynolds equation is solved simu...