Control of cast iron and casts manufacturing by Inmold method
Journal Title: Archiwum Odlewnictwa - Year 2009, Vol 9, Issue 3
Abstract
In this paper the usability of cast iron spheroidizing process in mould control by ATD method as well as by ultrasonic method were presented. Structure of instrumentation needed for control form performance of cast iron spheroidizing by Inmold method was illustrated. Author, pointed out that amount of magnesium master alloy should obtain 0,8 ÷ 1,0% of mass in form at all. Such quantity of preliminary alloy assure of obtain of nodular graphite in cast iron. In consequence of this, is reduce the cast iron liquidus temperature and decrease of recalescence temperature of graphite-eutectic crystallization in compare with initial cast iron. Control of casts can be carried out by ultrasonic method. In plain cast iron, ferritic-pearlitic microstructure is obtaining. Additives of 1,5% Cu ensure pearlitic structure.
Authors and Affiliations
S. Pietrowski
Keywords
Related Articles
- EP ID EP72022
- DOI -
- Views 79
- Downloads 0
Refining processes of selected copper alloys
The analysis of the refining effectiveness of the liquid copper and selected copper alloys by various micro additions and special refining substances – was performed. Examinations of an influence of purifying, modifying...
Ultrasonic methods for the tests of quality of casts from the alloys of aluminum
In this work we present the results of the check test of the properties of casts, made by the method of smelted models in the precise foun-dry THE ARMATURA in Lodz. Casts were made according to the new technological solu...
The influence of amperage of electric arc on microhardness in the area single and overlapping remeltings of HS 6-5-2 steel
The present thesis depicts the microhardness of HV0,065 surface layer of high speed steel HS6-5-2 remelted with the electric arc. There were different surface layer variants of remelting used – the amperage was changed f...
The comparison of the structure and microhardness of the tool steel C90 and HS 6-5-2 remelted with the electric arc
The examination of the structure and microhardness of surface layer of C90 non-alloy steel and HS 6-5-2 high speed steel after electric arc treatment are presented in the paper. The comparison has been presented due to t...
Use of the JM- SPC software to statistical control of high pressure die casting production-variable valued data type
Usefulness of the JM-SPC computer program for a statistical analysis of variable valued data proceeded from an Al-Si high-pressure die casting production processes was examined. An analysis subject were results of dimens...