Effect of post-weld heat treatment on thermal diffusivity in UNS S32304 duplex stainless steel welds
Journal Title: Archives of Materials Science and Engineering - Year 2017, Vol 2, Issue 88
Abstract
Purpose: The thermal diffusivity variation of UNS S32304 duplex stainless steel welds was studied after pulsed GTA welding autogenous process without filler addition. This property was measured in the transverse section of thin plates after welding process and post-heat treated at 750°C for 8 h followed by air-cooling. Design/methodology/approach: The present work reports measurements of thermal diffusivity using the laser-flash method. The thermal cycles of welding were acquired during welding by means of k-type thermocouples in regions near the weld joint. The used shielding gas was pure argon and 98% argon plus 2% of nitrogen. The temperature profiles were obtained using a digital data acquisition system. Findings: It was found an increase of thermal diffusivity after welding process and a decrease of these values after the heat treatment regarding the solidified weld pool zone, irrespective of the welding protection atmosphere. The microstructure was characterized and an increase of austenite phase in the solidified and heat-affected zones was observed for post-weld heat-treated samples. Research limitations/implications: It suggests more investigation and new measurements about the influence of the shielding gas variation on thermal diffusivity in the heat-affected zone. Practical implications: The nuclear industry, especially, requests alloys with high thermal stability in pipes for power generation systems and safe transportation equipment’s for radioactive material. Thus, the duplex stainless steel grades have improved this stability over standard grades and potentially increase the upper service temperature reliability of the equipment. Originality/value: After heat treatment, the welded plate with 98%Ar plus 2%N2 as shielding gas presented a thermal diffusivity closer to the as received sample. By means of 2%-nitrogen addition in shielding gas during GTAW welding of duplex stainless steel may facilitate austenite phase reformation, and then promotes stability on the thermal diffusivity of duplex stainless steels alloys.
Authors and Affiliations
E. G. Betini, C. S. Mucsi, T. S. Luz, M. T. D. Orlando, M-N. Avettand-Fènoël, J. L. Rossi
Keywords
Related Articles
- EP ID EP254122
- DOI 10.5604/01.3001.0010.8039
- Views 67
- Downloads 0
Surface morphology and topographical studies of fluorine doped tin oxide as transparent conducting film
Purpose: This paper deals about the preparation and characterization of transparentconducting metal oxide doped with fluorine for superhydrophobic applications.Design/methodology/approach: Fluorine doped tin oxide(FTO) h...
Functionalization of technical textile tapes
Purpose: The aim of the study was to deposit a hydrophobic barrier coating on technical tapes in order to protect them from water and to test and assess the obtained products. Design/methodology/approach: The coatings we...
Microstructure and mechanical properties of the annealed 6060 aluminium alloy processed by ECAP method
Purpose: The main goal of this paper is to present the investigation results of microstructuralevolution and mechanical properties changes in commercial EN AW 6060) aluminium alloyafter intensive plastic deformation, obt...
The properties of experimental silicones reinforced with silica fillers for dentistry
Purpose: Silicone materials crosslinked during the hydrosilylation reaction are common indental prosthetics and dentistry. These materials are characterized by a relatively very goodproperties. However, one of the fundam...
Application of QFD & VE & lean approach for control tests in a product design
Purpose: of this paper consists of identifying and prioritising control tests of a product design with integrating QFD and VE techniques according to use of the lean approach to increase the productivity o...