Heat resistance of Fe-Al intermetallics in the context of selected heat-resistant and hihg-temperature creep resistant steels
Journal Title: Archiwum Odlewnictwa - Year 2009, Vol 9, Issue 2
Abstract
Results are hereby presented of heat-resistance tests of two Fe3Al and FeAl intermetallic phase-based alloys in the context of St41k-type boiler steel and 50H21G9N4 high-temperature creep resistant steel. It has been ascertained that heat resistance of the 50H21G9N4 steel and of the Fe3Al and FeAl intermetallic phase-based alloys significantly exceeds that of the boiler steel tested in the air atmosphere and the atmosphere of a flue gas with CO, CO2, SiO2 content alike. Improvement of these properties depends of exposure conditions. The largest differences have been observed when the tests were carried out in temperature 1023 K and in the flue gas atmosphere. The differences have been more and more noticeable as the exposition duration extended. A tendency has been also recorded of smaller mass decrements of the Fe3Al and FeAl intermetallic phase-based alloys as compared to the 50H21G9N4 steel.
Authors and Affiliations
A. Patejuk, M. Gawrylewski, P. Baranowski
Keywords
Related Articles
- EP ID EP70539
- DOI -
- Views 102
- Downloads 0
Influence of a matrix on properties of mottled cast iron applied for mill rolls
Mill rolls are ones of the most expensive tools applied in plastic working processes and have to satisfy several criteria, which allow them to be used. Cast iron mill rolls, due to their fracture toughness and tribologic...
Evaluation of fractures in MAR-M509 alloy samples after fatigue strength tests
The paper presents the result of fracture analysis in MAR-M509 samples after high-cycle bending fatigue strength tests. Microstructural tests were carried out with a scanning electron microscope. To identify carbide phas...
Selected aspects of the piece production of iron alloy castings in terms of their environmental impact
Problems of environmental protection are nowadays one of the top priorities in a policy programme adopted by the European Community. Reducing the negative impact of the domestic foundry industry on environment should res...
Effect of gas corrosion on the character of phase boundaries in Ni3Al / WC composite
In view of quite specific physico-chemical and performance properties, the composite based on an intermetallic Ni3Al compound reinforced with tungsten carbides (WC) was selected for investigations. The said composite is...
Gas flow through a multilayer ceramic mould in lost wax foundry process
The paper deals with the issues of permeability testing of ceramic moulds used in lost wax foundry process. The main issue in the testing is to provide proper specimens of ceramic moulds (CM). The moulds have to be repea...