Lateral and Perpendicular Thermal Conductivity Measurement on Textile Double Layers
Journal Title: Fibres and Textiles in Eastern Europe - Year 2015, Vol 23, Issue 4
Abstract
In this paper, the temperature distribution on a double layered fleece textile was measured experimentally with infrared thermography. A theoretical model based on the thin plate theory was to interpret the results measured. A two dimensional simulation of the same problem was carried out as well. By fitting the experimental data with the models, thermal conductivities in the lateral and perpendicular directions could be determined.
Authors and Affiliations
Mariusz Felczak, Gilbert De Mey, Bogusław Więcek, Marina Michalak
Keywords
Related Articles
- EP ID EP69006
- DOI -
- Views 115
- Downloads 0
Wpływ długości i przygotowania włókien na mechaniczne właściwości hybrydowych przędz z włókien węglowych i poliamidowych oraz wykonanych z nich kompozytów
Celem badań było stwierdzenie wpływu długości włókien węglowych i ich obróbki przed zgrzebleniem na mechaniczne właściwości przędz hybrydowych/włókno węglowe /poliamid 6/ jak również kompozytów z nich wykonanych. Zmienia...
Warp-knitted Fabric Defect Segmentation Based on the Shearlet Transform
The Shearlet transform has been a burgeoning method applied in the area of image processing recently which, differing from the Wavelet transform, has excellent properties in processing singularities for multidimensional...
Investigation of the Effect of Pile Height and Yarn Linear Density on the Performance Properties of Pile Loop and Cut-Pile Loop Knit Fabrics
This paper investigates the effects of fabric structural parameters such as pile yarn linear density (19.7, 22.7 and 24.6 tex), ground yarn linear density (100 and 78 dtex), sinker height (2.2 sinker; 2.5 sinker and 2.8...
Obtaining New Biopolymer Materials by Electrospinning
The paper covers aspects of the technology of fibre electrospinning for the production of nonwoven fabrics for various application areas. The conditions of forming nano- and microfibres from solutions of collagen hydroly...
Właściwości kompozytów aramidowych i z polietylenu o super wysokim ciężarze cząsteczkowym poddanych udarom o małej prędkości
Powszechną metodą produkcji kompozytów dla zastosowań balistycznych jest użycie jako wzmocnienia włókien aramidowych oraz włókien polietylenowych o super wysokim ciężarze cząsteczkowym i różnych materiałach matrycy. Mate...