Macroscopic quality evaluation of lacquered steel sheets
Journal Title: Production Engineering Archives - Year 2014, Vol 0, Issue 1
Abstract
This paper deal with the evaluation of quality of lacquered sheets with different pre-treatments after corrosive loading. Samples will be divided into groups according to the type and duration corrosion loadings. After exposure to corrosive salt mist corrosion chamber, the samples will be evaluated macroscopically according to relevant standards. Low degradation after all time corrosion load was on the sample pre-treated with an alkaline degreasing in combination with a yellow chromating and the samples pre-treated with an alkaline de-greasing in combination with surface passivation. On these samples showed no loss of adhesion to the base material and the evaluation of delamination due to corrosion during loading had a low degree of degradation. Surfaces after the cross-cut test did not for both sets of sam-ples after corrosion load all times no defects in the adhesion layer.
Authors and Affiliations
Jaroslava Svobodová, Sylvia Kuśmierczak
Keywords
Related Articles
- EP ID EP165635
- DOI -
- Views 129
- Downloads 0
How can people be convinced to buy electric cars? – case of Slovenia
Electric cars represent a promising energy-and carbon-efficient alternative to internal combustion en-gine cars. However, as mobility behaviour is highly habitual, convincing people to switch from con-ventional cars to e...
Statistical analysis of responses concerning the importance of human and production or services issues in various companies
In the article the results of statistical analysis is presented with the use of basic statistical parameters and box and whisker plot conducted for the dataset, containing answers to the question E9 from BOST survey. Mea...
Microstructural evaluation of the lacquered layer quality after corrosion load
Surface pre-treatment is one of the most important steps before applying the final surface treatment. These pre-treatments, like phosphating, alkaline degreasing, pickling in acids, is used to remove impurities from the...
Analysis of risk of nonconformities and applied quality inspection methods in the process of aluminium profiles coating based on FMEA results
In the aerospace industry, passenger safety depends on proper quality control at each production stage. The main responsibility for the correct operation of the aircraft lies within a gas turbine. A proper and rigorous s...
LEAN Production issues in the organization of the company - the first stage
Today's market determinants and most importantly, very dynamically changing customer requirements significantly shortened the product life cycle. This situation reflects in companies by common exten-sion of the assortmen...