The healing of damage after the plastic deformation of metals
Journal Title: Frattura ed Integrità Strutturale - Year 2013, Vol 7, Issue 24
Abstract
The general regularities of damage healing during the annealing after cold deformation of metal materials are presented in this paper. In categories of damage mechanics the kinetic equations of damage healing during recovery and recrystallization are formulated. Diagrams of damage healing for some metal alloys are presented. The example of use of investigation results for optimization of industrial technology of pipes drawing is presented.
Authors and Affiliations
S. V. Smirnov
Keywords
Related Articles
- EP ID EP156522
- DOI 10.3221/IGF-ESIS.24.02
- Views 69
- Downloads 0
Designing aluminium friction stir welded joints against multiaxial fatigue
The present paper investigates the accuracy of the Modified Wöhler Curve Method (MWCM) in estimating multiaxial fatigue strength of aluminium friction stir (FS) welded joints. Having developed a bespoke joini...
Fracture mechanics analyses of the slip-side joggle regions of wing-leading-edge panels
The Space Shuttle wing-leading edge consists of panels that are made of reinforced carbon-carbon. Coating spallation was observed near the slip-side region of the panels that experience extreme heating. To understand t...
Comparison of two multiaxial fatigue models applied to dental implants
This paper presents two multiaxial fatigue life prediction models applied to a commercial dental implant. One model is called Variable Initiation Length Model and takes into account both the crack initiation and...
Damages to stent stabilized left ventricular pacemaker electrodes during simulated lead extraction
During biventricular pacemaker implantation stents can be applied for coronary sinus lead stabilization to prevent lead dislocations. A lot of issues have been raised in connection with the use of the stent. In some case...
Use of Circumferentially Cracked Bar sample for CTOD fracture toughness determination in the upper shelf regime
In this work, the use of circumferentially cracked bar (CCB) sample to determine material fracture toughness in the upper shelf regime for carbon steels has been investigated. Since high fracture toughness materi...