THE ANALYSIS OF WEAR OF THE LAYERS CONTAINING WC/W2C IN ABRASIVE SOIL
Journal Title: Tribologia - Year 2016, Vol 269, Issue 5
Abstract
The paper presents the results of research involving the resistance of hardfacing materials containing WC/W2C carbides to abrasive wear. The tested hardfacing materials were made using PJ5D and El-Tung FeA rods. The WC/W2C carbide contents of the examined materials amounted to 90% and 60%. These materials are meant to be used in mining tools subject to intense abrasive wear. In spite of its higher WC/W2C carbide content, the intensity of wear of the hardfacing material made using the PJ5D rod was higher than that of the hardfacing material made using the El-Tung FeA rod. Wear resistance tests were conducted by means of the “spinning bowl” method, using real (natural) soil masses. Light and heavy soil masses were used.<br/><br/>
Authors and Affiliations
Jerzy NAPIÓRKOWSKI, Krzysztof LIGIER
Keywords
Related Articles
- EP ID EP241330
- DOI 10.5604/01.3001.0010.6612
- Views 64
- Downloads 0
TRIBOLOGICAL PROPERTIES OF NICKEL ELECTROLITYCAL ALLOYS AFTER HEAT TREATMENT
This paper describes the tribological properties (linear wear) of the electrolytic coatings containing nickel alloys, Ni-Mo and Ni-W, which contain carbides forming elements. These coatings were also subjected to heat tr...
EFFECT OF COARSE-TO-FINE WC GRAIN RATIO ON MECHANICAL PROPERTIES AND ABRASIVE WEAR OF WC-8Co CEMENTED CARBIDES
This study performs a comprehensive analysis concerning the amount of fine tungsten carbide (WC) grains needed for the appropriate reinforcement of the cobalt (Co) metallic binder in WC-8Co cemented carbides. The goal is...
POSSIBILITIES OF SHAPING THE WEAR RESISTANCE OF THE LASER BORONIZED SURFACE LAYERS ON MACHINE PARTS PRODUCED WITH STEEL AND CAST IRON
This paper presents the importance of laser techniques in shaping parts of surface layers with cast iron and steel. Laser boronizing was carried out using a CO2 laser with a nominal power of 2600W for multiple tracks. La...
MIKROSTRUKTURA I ODPORNOŚĆ NA ZUŻYCIE ŚCIERNO-KOROZYJNE WARSTWY CHROMOKRZEMOWANEJ NA STALI C45
Omówiono wyniki badań dotyczące mikrostruktury warstwy chromokrzemowanej wytworzonej na podłożu stali C45 w kształtowaniu odporności na zużycie podczas tarcia ścierno-korozyjnego. Proces chromokrzemowania realizowano prz...
TRIBOLOGICAL PROPERTIES OF CRC+CRN TYPE HYBRID LAYERS PRODUCED IN COMBINED VACUUM CHROMIZING PROCESS AND PVD TREATMENT
Tribological properties of the CrC+CrN type hybrid layers, produced on X210Cr12 steel in vacuum chromizing process combined with arc evaporation PVD treatment, have been investigated. A comparison of the CrC+CrN type hyb...