The influence of modification and squeeze casting on properties of AlSi11 alloy castings
Journal Title: Archiwum Odlewnictwa - Year 2011, Vol 11, Issue 2
Abstract
The results of structural examinations and tests of mechanical properties of AlSi11 alloy, either gravity or squeeze cast, have been presented. The investigations have been carried out for both the non-modified silumin and the alloy modified with AlSr10 strontium master alloy. The measurements have been carried out for the cast plates of dimensions 200×100×25 mm. It has been found out that the modification combined with squeeze casting provides an advantageous set of strength and plastic properties (RBmB ≈ 270 MPa, AB5B ≈ 16%). The metallographic examination has revealed a significant refinement of both the primary α-phase dendrites and the silicon eutectics, however being dependent on the method of modification and casting. It has been found that the refinement of the primary crystals results from the influence of external pressure exerted on the solidifying casting, while the refinement observed for silicon eutectics is an effect of combined influence of modification and squeeze casting.
Authors and Affiliations
A. Zyska, Z. Konopka, M. Łągiewka
Keywords
Related Articles
- EP ID EP72636
- DOI -
- Views 112
- Downloads 0
Macrostructure of IN-713C superalloy after volume modification
The study discusses the results of the preliminary investigations of the process of volume modification of nickel and cobalt superalloys. The investigations were carried out on an IN-713C alloy. As an inoculant, cobalt a...
The influence of the conditions of gypsum plaster preparation on its technological properties
The results of researches on influence of basic preparation parameters, i.e. time and mixing intensity, start and end time of set, dimensional changes and strength of gypsum plaster, are presented in this paper. Determi...
Usage of Connor Inlets to Eliminate Shrinkage
The demand for castings of high quality and sound work is nowadays very high. The production of sound castings without foundry errors is the big issue in modern foundries. Foundry simulation software can do a lot to help...
Effect of alloying elements on branching of primary austenite dendrites in Ni-Mn-Cu cast iron
Within the research, determined were direction and intensity of influence of individual alloying elements on branching degree of primary austenite dendrites in austenitic cast iron Ni-Mn-Cu. 30 cast shafts dia. 20 mm wer...
The assessment of hot cracking susceptibility of ferritic-austenitic cast iron
An inspiration to the research work has arisen from the problems related to cracking of massive castings made of ferritic-austenitic cast steel. The shape and the character of crack trajectories indicate that they are ho...