The influence of remelting parameters of the electric arc and conventional tempering on the tribological resistance of high speed steel HS 6-5-2
Journal Title: Archiwum Odlewnictwa - Year 2011, Vol 11, Issue 3
Abstract
The present thesis depicts the results of the research of tribological high speed steel HS 6-5-2 remelted with the electric arc. Steel was remelted with different parameters. The amperage of electric arc was changed, the scanning speed was changed and the single, overlapping remeltings were used. There was also the influence of conventional tempering defined, which was conducted after remelting on the tribological resistance of hardened steel. For the previously mentioned processing variants, the intensity of tribological wear was defined and the linear wear were presented, and the friction coefficients. The type of tribological wear was also given, present during the friction, technically dry, of the hardened steel. The lower intensity of tribological wear was received for the single remelting by electric arc of 50 and 70A. Using the overlapping remeltings for the strengening of the surface layer of the high speed steel HS 6-5-2 causes the increase of the intensity of tribological wear in comparison to the steel with the single remelting. The conventional tempering leads to the decrease of the intensity of tribological wear.
Authors and Affiliations
A. Dziedzic
Keywords
Related Articles
- EP ID EP72287
- DOI -
- Views 120
- Downloads 0
Influence of selected modifiers on crystallization curve of chromium cast iron
In article was introduced the results of investigations of modified chromium cast iron crystallization process. It the cast iron about composition of basic elements C = 2,8 % and Cr = 18% was modified with five substance...
Influence of pressure mould material on the durability of coating a thermal and anti-erosion barrier
This study presents the research results of the durability of coating (thermal and anti-erosion barrier) of a mincer cap casting pressure mould. Tests were conducted with the use of an IDRA OL320 pressure machine. Durabi...
Influence of vibrations during crystallization on mechanical properties and porosity of AlSi11 alloy
Autorka artykułu podjęła się omówienia problematyki opieki duszpasterskiej nad uchodźcami-katolikami w Imperium Rosyjskim w latach pierwszej wojny światowej. Zapewnienie uchodźcom opieki religijnej było jednym z ważniejs...
Analysis of the failure causes in an element made of AlSi11Cu2(Fe) alloy
The paper presents results of research on a cross element damaged during the service, made of the casting alloy of aluminum - AlSi11Cu2(Fe) (AK132). Performed research was to explain the reasons for this damage and inclu...
Influence of heat treatment on microstructure and properties of GX12CrMoVNbN9-1 cast steel
The paper presents results of research on the influence of multistage heat treatment on microstructure and properties of high-chromium martensitic GX12CrMoVNbN9 – 1 (GP91) steel. The material under investigation were sam...