Investigation into the Dielectric Properties of Polypyrrole Coated Fabrics Composites
Journal Title: Fibres and Textiles in Eastern Europe - Year 2019, Vol 27, Issue 5
Abstract
Flexible polypyrrole coated fabric composites with good dielectric properties were produced using pyrrole as a monomer by in-situ polymerisation on polyester fabric. Initially, the influence of the pyrrole concentration, temperature and time on the dielectric constant of the real and imaginary parts, the loss tangent, and the surface resistance of the composites were investigated. Subsequently, exterior morphologies was analysed. The results show that the pyrrole concentration, the reaction temperature and time had a significant influence on the real and imaginary parts of the dielectric constant, the loss tangent, and the surface resistance of the composites. The polypyrrole composites produced show good performance in terms of dielectric properties and electrical conductivity.In the 0-106 Hz frequency range, the values of the real and imaginary parts of the dielectric constant of the 0.8 mol/L group are both at their largest. Moreover, the value of the surface resistance of the 0.8 mol/L group is at its smallest, and the value of the surface resistance of the 0.2 mol/L group is at its largest, which is 12 times the value given by the 0.8mol/L group.Values of the real and imaginary parts of the dielectric constant, and the loss tangent for the experimental group produced by polymerisation at ambient temperature are at their largest, which is superior to the other groups. The value of the surface resistance for the experimental group produced at ambient temperature is at its smallest and the electrical conductivity is at its strongest; the higher the reaction temperature, the larger the value of the resistance. The various dielectric properties of the 150 min group are better than for the other groups.<br/><br/>
Authors and Affiliations
Chuanbing Ge, Yuanjun Liu, Xiaoming Qian
Keywords
Related Articles
- EP ID EP600872
- DOI 10.5604/01.3001.0013.2905
- Views 98
- Downloads 0
Experimental Studies on the Dielectric Behaviour of Polyester Woven Fabrics
In this paper, the influence of fabric structure, weft density, end spacing and yarn fineness on the dielectric constant of polyester woven fabrics was studied. The results show that at low frequencies, the dielectric co...
Experimental Investigation of the Relationship Between the Yarn Tension and Bobbin Diameter in the Warping Process
Yarns of different types are unwound from bobbins in different processes like warping, weaving, doubling and re-winding. A change in yarn tension from a full to empty bobbin causes serious product quality and machine eff...
Cottonisation of Decorticated Flax Fibres
The commonly used flax process of decortication allows the mechanical extraction of fibre from plant stems without prior retting. The one-type fibre obtained in this process is characterised by very low quality, as it is...
Optymalizacja właściwości określających komfort dzianin o splocie lewoprawym
Głównym celem pracy było zbadanie wpływu parametrów struktury dzianiny takich jak długość pętli, współczynnik zapełnienia, typ włókna i właściwości przędzy na mechaniczne i związane z komfortem właściwości dzianin lewopr...
Influence of Fibre Length and Preparation on Mechanical Properties of Carbon Fibre/Polyamidea 6 Hybrid Yarns and Composites
The aim of this paper was to investigate the effect of carbon fibre (CF) length and preparation prior to carding on the mechanical properties of hybrid yarns as well as composites consisting of CF and polyamide 6 (PA 6)....